product name | Fire reaction class | Sizes | Thermal conductivity coefficient | Compression tensions | Tensile strength | Long-term water absorption | # |
---|---|---|---|---|---|---|---|
E class | On request | ≤0,036 W/m*K | ≥27,3 kPa | ≥200 kPa | ≤5% | ![]() DOBELES PANELIS ST Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Long-term water absorption | |
not specified | On request | ≤0,034 W/m*K | ≥40,9 kPa,≥54,5 kPa | ≥150 kPa,≥200 kPa | ≤5% | ![]() TENAPORS L EPS Sizes Fire reaction class Thermal conductivity coefficient Long-term water absorption Insulation thickness | |
not specified | On request | ≤0,034 W/m*K | ≥54,5 kPa | ≥200 kPa | ≤5% | ![]() DOBELES PANELIS P Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
not specified | On request | ≤0,034 W/m*K | ≥54,5 kPa | ≥200 kPa | ≤5% | ![]() DOBELES PANELIS S Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | 1200×600 mm | ≤0,034 W/m*K | ≥40,9 kPa | ≥150 kPa | ≤5% | ![]() TENAPORS TERMO Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | 1200×600 mm | ≤0,034 W/m*K | ≥40,9 kPa | ≥150 kPa | ≤3,5% | ![]() | |
E class | 1200×600 mm | ≤0,036 W/m*K | ≥32,7 kPa | - | ≤3,5% | ![]() TENAPORS SUPRA Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Steam resistances Long-term water absorption | |
E class | 1200×600 mm | ≤0,036 W/m*K | ≥27,3 kPa | ≥100 kPa | ≤3,5% | ![]() TENAPORS PRIMA Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption | |
E class | 1000×500* mm | ≤0,031 W/m*K | ≥40,9 kPa | ≥150 kPa | ≤3,5% | ![]() TENAPORS NEO EPS 150 Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
- | 1000×500* mm | ≤0,031 W/m*K | ≥27,3 kPa | ≥100 kPa | ≤3,5% | ![]() TENAPORS NEO EPS 100 Sizes Thermal conductivity coefficient Compression tensions Tensile strength Long-term water absorption Insulation thickness | |
- | 1000×500* mm | ≤0,031 W/m*K | ≥21,8 kPa | ≥80 kPa | ≤3,5% | ![]() TENAPORS NEO EPS 80 Sizes Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | 1000×500* mm | ≤0,040 W/m*K | It is not recommended to use in load bearing structures | - | ≤5% | ![]() TENAPORS EPS 60 Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Steam resistances Long-term water absorption Insulation thickness | |
E class | 1000×500* mm | ≤0,032 W/m*K | It is not recommended to use in load bearing structures | ≥70 kPa | ≤3,5% | ![]() TENAPORS NEO EPS 70 Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | 1000×500* mm | ≤0,034 W/m*K | ≥54,5 kPa | ≥200 kPa | ≤5% | ![]() TENAPORS EPS 200 Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | 1000×500* mm | ≤0,036 W/m*K | ≥32,7 kPa | - | - | ![]() TENAPORS EPS 120 Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Steam resistances Insulation thickness | |
- | 1000×500* mm | ≤0,036 W/m*K | ≥27,3 kPa | ≥100 kPa | ≤5% | ![]() TENAPORS EPS 100 Sizes Thermal conductivity coefficient Compression tensions Tensile strength Long-term water absorption Insulation thickness | |
- | 1000×500* mm | ≤0,037 W/m*K | ≥21,8 kPa | ≥80 kPa | ≤5% | ![]() TENAPORS EPS 80 Sizes Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
- | 1000×500* mm | ≤0,039 W/m*K | It is not recommended to use in load bearing structures | ≥70 kPa | ≤5% | ![]() TENAPORS EPS 70 Sizes Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | 1000×500* mm | ≤0,036 W/m*K | ≥32,7 kPa | - | ≤5% | ![]() TENAPORS EPS 150 Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Steam resistances Long-term water absorption Insulation thickness | |
not specified | 1100x800mm | ≤0,034 W/m*K | ≥40,9 kPa | ≥150 kPa | ≤5% | ![]() TENAPORS TERMO COMPACT Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
E class | Insulation thickness 30 - 200 mm,Length 1200mm,Diameter 10 - 1000 mm | ≤0,036 W/m*K | ≥27,3 kPa | ≥100 kPa | ≤5% | ![]() TENAPORS T Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness | |
not specified | On request | ≤0,034 W/m*K | ≥54,5 kPa | ≥200 kPa | ≤5% | ![]() TENAPORS DECOR Sizes Fire reaction class Thermal conductivity coefficient Compression tensions Tensile strength Steam resistances Long-term water absorption Insulation thickness |